Acrylic Resin for Denture Base
BASIS HI is an acrylic elastomere, high impact resistance heat-curing resin for denture bases.
An adaptable and aesthetically pleasing denture of excellent temperature stability is achievable without any air bubble formation or shrinkage.
High impact resistance – guarantees worry-free application and use for patients and dental professionals.
Heat-Curing Method: Immerse the flask in a container of tap water.
Apply heat gradually for about 30minutes until boil.
Let the resin completely cure for 30 – 40 minutes in boiling water.
Cool the flask for about 30 minutes at room temperature.
Recover denture after cooling completely.
Heat-Curing Method: Immerse the flask in a container of tap water.
Apply heat until boil. Let the resin completely cure for 30 – 40 minutes (Curing time starts when the water with the flask has started to boil).
Cool the flask for about 30 minutes at room temperature.
Recover denture after cooling completely.
Packing | Retail |
---|---|
Powder | 1kg 3kg 10kg |
Liquid | 500mL (Pipette x 1) 1L 17L |
Shades | |
All shades are vein fibers-containing shades. |
Powder/Liquid Mixing Ratio, g:mL | 100 : 43 |
---|---|
Flexural Strength, MPa | 112.7 |
Flexural Modulus, MPa | 2400 |
Vickers Hardness, Hv | 19.5 |
Sorption, μg/mm3 | 24 |
Solubility, μg/mm3 | 1.2 |
Residual Monomer, wt% | 0.7 |
* Please use with the BASIS Liquid.