BASIS HI
Acrylic Resin for Denture Base
– Since it is more impact-resistant than standard denture base resin, the thickness of the base can be made thinner.
Heat-Curing Method: Immerse the flask in a container of tap water.
Apply heat until boil. Let the resin completely cure for 30 – 40 minutes (Curing time starts when the water with the flask has started to boil).
Cool the flask for about 30 minutes at room temperature.
Recover denture after cooling completely.
| Packing | Retail |
|---|---|
| Powder | 1kg 3kg 10kg |
| Liquid | 500mL (Pipette x 1) 1L 17L |
| Shades |     |
| All shades are vein fibers-containing shades. |
Physical Properties
| Powder/Liquid Mixing Ratio, g:mL | 100 : 43 |
|---|---|
| Flexural Strength, MPa | 112.7 |
| Flexural Modulus, MPa | 2400 |
| Vickers Hardness, Hv | 19.5 |
| Sorption, μg/mm3 | 24 |
| Solubility, μg/mm3 | 1.2 |
| Residual Monomer, wt% | 0.7 |
* Please use with the BASIS Liquid.