Self-Curing Acrylic Resin for Patterns

 

PATTERN BRIGHT is a self-curing resin for various pattern applications.
With its very low polymerization shrinkage, as minimum as 0.72%, a compatible and satisfactory pattern is achieved.
Hardening time is designed for speedy-work completion.
When brush method is used, pattern production is made easy thanks to its excellent viscosity property.
An almost no incineration residue results to smooth surface of the casting body, thus requires only minimal polishing.
It can also be used to create jigs for implant cases.

 

Usage Making out patterns on metal plates, lingual bars, palatal bars and connectors
Production of patterns on various clasps
Production of various Konuskronen telescope exterior crown patterns
Production of bonded bridge patterns
Temporary bonding of worn wax
Making jigs for implant cases
Packing 1-1Set Retail
Powder 100 g 100 g
Liquid 100 mL 100 mL
Accessories (Silicon Cup, Paint Brush, Pipette) x 1 each Pipette x 1
Shade PINK

 

Physical Properties
Powder/Liquid Mixing Ratio, g:mL 100 : 50
*Hardening Time (23℃) 3min 20sec
Vickers Hardness, Hv 13.4
Flexural Strength, MPa 60
Post Setting Shrinkage
(23℃), %		 After 30 minutes 0.05%
After 24 hours 0.06%
Polymerization Shrinkage (23℃), % 0.72%
Incineration Residue (700℃), % 0.067%

* Hardening time value using prescribed powder/liquid mixing ratio at 23℃.
Hardening time at lower and higher room temperature will become longer and shorter, respectively.